A series of CuO/Al2O3 catalyst-sorbents have been subjected to a large number of reaction-regeneration cycles and their physical and chemical properties compared before and after operation. The reaction phase of the cycle involved exposing the catalyst-sorbents to a mixture of SO2, NO, NH3, O-2, and steam at 350 degrees C, during which time NO conversion was always greater than 90% and the SO2 was converted into CuSO4. The regeneration phase involved reduction of CuSO4 to copper metal by CH4 at 500 degrees C, followed by oxidation in air at 450 degrees C. In some tests the reaction or regeneration conditions were made more severe in an attempt to accelerate deactivation. The SO2 sorption capacity of one sample, which had been subjected to 1525 cycles, was reduced by about 25%, but generally there was no significant change in reactivity. Small changes in physicochemical properties are interpreted in terms of redispersion of the supported copper phase.